| 品牌 | 三井化學(xué) |
|---|---|
| 貨號(hào) | TPX MBZ230 |
| 用途 | 工程應(yīng)用 |
| 牌號(hào) | TPX MBZ230 |
| 型號(hào) | TPX MBZ230 |
| 品名 | TPX |
| 外形尺寸 | 來(lái)電詢問(wèn) |
| 生產(chǎn)企業(yè) | 三井化學(xué) |
| 是否進(jìn)口 | 是 |
三井化學(xué)高透氣TPX MBZ230
|
Density / Specific Gravity |
1.10 |
g/cm? |
Internal Method |
|
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) |
57 |
g/10 min |
Internal Method |
|
Spiral Flow 3 |
48.0 |
cm |
Internal Method |
|
Molding Shrinkage 4 |
|
|
Internal Method |
|
Flow : 2.00 mm |
1.5 |
% |
|
|
Across Flow : 2.00 mm |
1.1 |
% |
|
|
Water Absorption (Saturation) |
0.040 |
% |
ASTM D570 |
| Hardness |
Nominal Value |
Unit |
Test Method |
|
Rockwell Hardness (R-Scale) |
84 |
|
ASTM D785 |
| Mechanical |
Nominal Value |
Unit |
Test Method |
|
Tensile Modulus 5 (23°C, Injection Molded) |
2250 |
MPa |
ASTM D638 |
|
Tensile Strength 5 |
|
|
ASTM D638 |
|
Yield, 23°C, Injection Molded |
27.0 |
MPa |
|
|
Break, 23°C, Injection Molded |
26.0 |
MPa |
|
|
Tensile Elongation 5 (Break, 23°C, Injection Molded) |
20 |
% |
ASTM D638 |
|
Flexural Modulus 6 (3.20 mm, Injection Molded, 51.0 mm Span) |
1820 |
MPa |
ASTM D790 |
|
Flexural Strength 6 (3.20 mm, Injection Molded, 51.0 mm Span) |
40.0 |
MPa |
ASTM D790 |
| Impact |
Nominal Value |
Unit |
Test Method |
|
Notched Izod Impact (Injection Molded) |
99 |
J/m |
ASTM D256 |
|
Unnotched Izod Impact 7 (23°C, Injection Molded) |
56 |
J/m |
ASTM D4812 |
| Thermal |
Nominal Value |
Unit |
Test Method |
|
Deflection Temperature Under Load 8 (0.45 MPa, Unannealed, 6.35 mm) |
145 |
°C |
ASTM D648 |
|
Vicat Softening Temperature |
162 |
°C |
ASTM D1525 9 |
|
Peak Crystallization Temperature (DSC) |
233 |
°C |
ASTM D3418 |
|
CLTE - Flow (-10 to 160°C)
|
1.3E-4 |
cm/cm/°C |
Internal Method |